口腔疾病防治 ›› 2018, Vol. 26 ›› Issue (1): 56–60.doi: 10.12016/j.issn.2096-1456.2018.01.011

• 综述 • 上一篇    下一篇

新型钙硅材料在活髓保存治疗中的研究进展

孙妍 综述1,2(), 邹玲 审校1()   

  1. 1.口腔疾病研究国家重点实验室 国家口腔疾病临床医学研究中心 四川大学华西口腔医院牙体牙髓病科,四川 成都(610041)
    2. 温州医科大学附属口腔医院牙体牙髓病科,浙江 温州(325027)
  • 收稿日期:2017-04-27 修回日期:2017-09-24 发布日期:2018-08-31
  • 作者简介:

    【作者简介】 孙妍,医师,硕士, Email: 934001560@qq.com

  • 基金资助:
    四川省科技计划项目 (2015JY0260)

Current progress of calcium silicon-based materials for pulp-capping

Yan SUN1,2(), Ling ZOU1()   

  1. 1. State Key Laboratory of Oral Diseases & National Clinical Research Center for Oral Diseases & Dept. of Conservative Dentistry and Endodontics, West China Hospital of Stomatology, Sichuan University, Chengdu 610041, China;
    2. Department of Conservative Dentistry and Endodontics, School & Hospital of Stomatology Wenzhou Medical University, Wenzhou 325027, China;
  • Received:2017-04-27 Revised:2017-09-24 Published:2018-08-31

摘要:

活髓保存治疗是通过盖髓或牙髓切断术的方式,保存牙髓活力的治疗方法。盖髓材料在此过程中发挥隔绝感染、促进成牙本质细胞分化、形成修复性牙本质的重要作用。钙硅材料以其优良的机械性能、生物活性、生物相容性在活髓保存治疗中发挥重要作用。笔者就近年来在活髓保存治疗中应用的新型钙硅材料的研究进展作一综述。

关键词: 活髓保存, 盖髓材料, 修复性牙本质, 新型钙硅材料, 生物活性, 生物相容性

Abstract:

The aim of vital pulp therapy is to preserve vital, healthy pulp tissue through pulp capping or pulpotomy. Pulp-capping materials are applied to isolate infection, promote odontoblast differentiation and reparative dentine formation during the progress. Calcium silicon-based materials play significant roles in vital pulp therapy with their favorable mechanical properties, bioactivity and biocompatibility. The present paper will review current progress for these novel calcium silicon-based materials used in vital pulp therapy.

Key words: Vital pulp therapy, Pulp-capping materials, Reparative dentine, Novel calcium silicon-based materials, Bioactivity, Biocompatibility

中图分类号: 

  • R781.05
[1] Qureshi A, E S. Recent advances in pulp capping materials: an overview[J]. J Clin Diagn Res, 2014, 8(1): 316-321.
[2] Hermann B W.Dentin obliteration der wurzelkanalenachbehandlungmit calcium[J]. ZahnarztlRundschau, 1930, 39: 888-890.
[3] Karthikeson PS, Jayalakshmi S.Pulp capping Agents-a review[J]. J Pharm Sci Res, 2016, 8(6): 525-527.
[4] Bakland LK, Andreasen JO.Will mineral trioxide aggregate replace Calcium hydroxide in treating pulpal and periodontal healing complications subsequent to dental trauma? a review[J]. Dent Traumatol, 2012, 28(1): 25-32.
[5] Prati C, Gandolfi MG.Calcium silicate bioactive cements: Biological perspectives and clinical applications[J]. Dent Mater, 2015, 31(4): 351-370.
[6] Lee SJ, Monsef M, Torabinejad M.Sealing ability of a mineral trioxide aggregate for repair of lateral root perforations[J]. J Endod, 1993, 19(11): 541-544.
[7] Tawil PZ, Duggan DJ, Galicia JC. Mineral trioxide aggregate (MTA): its history, composition, and clinical applications[J]. Compend Contin Educ Dent, 2015, 36(4): 247-252; quiz 254, 264.
[8] Kim RJ, Kim MO, Lee KS, et al.An in vitro evaluation of the antibacterial properties of three mineral trioxide aggregate (MTA) against five oral bacteria[J]. Arch Oral Biol, 2015, 60(10): 1497-1502.
[9] Rodrigues EM, Cornélio ALG, Mestieri LB, et al.Human dental pulp cells response to mineral trioxide aggregate (MTA) and MTA Plus: cytotoxicity and gene expression analysis[J]. Int Endod J, 2017, 50(8): 780-789.
[10] Prati C, Gandolfi MG.Calcium silicate bioactive cements: Biological perspectives and clinical applications[J]. Dent Mater, 2015, 31(4): 351-370.
[11] Alshwaimi E, Majeed A, Ali AA.Pulpal responses to direct capping with betamethasone / gentamicin cream and mineral trioxide aggregate: histologic and Micro-Computed tomography assessments[J]. J Endod, 2016, 42(1): 30-35.
[12] Ghorbanzadeh A, Ghorbanzadeh A.Maturogenesis of two maxillary central incisors: a case report with 10 years of follow up[J]. J Dent (Tehran), 2015, 12(4): 306-315.
[13] Dharmani U, Jadhav GR, Kaur Dharmani CK, et al.Mineral trioxide aggregate pulpotomy in autotransplanted immature mandibular third molar with a 4-year follow-up[J]. J Conserv Dent, 2016, 19(3): 293-295.
[14] Hilton TJ, Ferracane JL, Mancl L, et al.Comparison of CaOH with MTA for direct pulp capping: a PBRN randomized clinical trial[J]. J Dent Res, 2013, 92(7 Suppl): 16S-22S.
[15] Mente J, Hufnagel S, Leo M, et al.Treatment outcome of mineral trioxide aggregate or calcium hydroxide direct pulp capping: long-term results[J]. J Endod, 2014, 40(11): 1746-1751.
[16] Çalışkan MK, Güneri P.Prognostic factors in direct pulp capping with mineral trioxide aggregate or Calcium hydroxide: 2- to 6-year follow-up[J]. Clin Oral Investig, 2017, 21(1): 357-367.
[17] Li Z, Cao L, Fan M, et al.Direct pulp capping with calcium hydroxide or mineral trioxide aggregate: a meta-analysis[J]. J Endod, 2015, 41(9): 1412-1417.
[18] Rasaratnam L.Review suggests direct pulp capping with MTA more effective than calcium hydroxide[J]. Evid Based Dent, 2016, 17(3): 94-95.
[19] Zhou HM, Shen Y, Wang ZJ, et al.In vitro cytotoxicity evaluation of a novel root repair material[J]. J Endod, 2013, 39(4): 478-483.
[20] Lee LW, Hsiao SH, Hung WC, et al.Clinical outcomes for teeth treated with electrospun poly(ε-caprolactone) fiber meshes/mineral trioxide aggregate direct pulp capping[J]. J Endod, 2015, 41(5): 628-636.
[21] Camilleri J.Investigation of biodentine as dentine replacement material[J]. J Dent, 2013, 41(7): 600-610.
[22] Aggarwal V, Singla M, Miglani S, et al.Comparative evaluation of push-out bond strength of ProRoot MTA, Biodentine, and MTA Plus in furcation perforation repair[J]. J Conserv Dent, 2013, 16(5): 462-465.
[23] Laurent P, Camps J, De Méo M, et al.Induction of specific cell responses to a Ca(3)SiO(5)-based posterior restorative material[J]. Dent Mater, 2008, 24(11): 1486-1494.
[24] Simsek N, Alan H, Ahmetoglu F, et al.Assessment of the biocompatibility of mineral trioxide aggregate, bioaggregate, and biodentine in the subcutaneous tissue of rats[J]. Niger J Clin Pract, 2015, 18(6): 739-743.
[25] Kim J, Song YS, Min KS, et al.Evaluation of reparative dentin formation of ProRoot MTA, Biodentine and BioAggregate using micro-CT and immunohistochemistry[J]. Restor Dent Endod, 2016, 41(1): 29-36.
[26] Borkar SA, Ataide I.Biodentine pulpotomy several days after pulp exposure: Four case reports[J]. J Conserv Dent, 2015, 18(1): 73-78.
[27] Grewal N, Salhan R, Kaur N, et al.Comparative evaluation of Calcium silicate-based dentin substitute (Biodentine(®)) and Calcium hydroxide (pulpdent) in the formation of reactive dentin bridge in regenerative pulpotomy of vital primary teeth: triple blind, randomized clinical trial[J]. Contemp Clin Dent, 2016, 7(4): 457-463.
[28] Rajasekharan S, Martens LC, Vandenbulcke J, et al.Efficacy of three different pulpotomy agents in primary molars: a randomized control trial[J]. Int Endod J, 2017, 50(3): 215-228.
[29] Camilleri J, Kralj P, Veber M, et al.Characterization and analyses of acid-extractable and leached trace elements in dental cements[J]. Int Endod J, 2012, 45(8): 737-743.
[30] Nielsen MJ, Casey JA, Vanderweele RA, et al.Mechanical properties of new dental pulp-capping materials[J]. Gen Dent, 2016, 64(1): 44-48.
[31] Zhang S, Yang X, Fan M.BioAggregate and iRoot BP plus optimize the proliferation and mineralization ability of human dental pulp cells[J]. Int Endod J, 2013, 46(10): 923-929.
[32] Zhu L, Yang J, Zhang J, et al.In vitro and in vivo evaluation of a nanoparticulate bioceramic paste for dental pulp repair[J]. Acta Biomater, 2014, 10(12): 5156-5168.
[33] Jiang S, Wu H, Zhang CF.Partial pulpotomy of immature teeth with apical periodontitis using bioceramics and mineral trioxide aggregate: a report of three cases[J]. Chin J Dent Res, 2016, 19(2): 115-120.
[34] Shi S, Zhang DD, Chen X, et al.Apical sealing ability of bioceramic paste and mineral trioxide aggregate retrofillings: a dye leakage study[J]. Iran Endod J, 2015, 10(2): 99-103.
[35] Guo YJ, Du TF, Li HB, et al.Physical properties and hydration behavior of a fast-setting bioceramic endodontic material[J]. BMC Oral Health, 2016, 16(1): 23.
[36] Jiang YQ, Zheng QH, Zhou XE, et al.A comparative study on root canal repair materials: a cytocompatibility assessment in L929 and MG63 cells[J]. Scientific World Journal, 2014, 2014(12): 463826.
[37] Lv F, Zhu L, Zhang J, et al.Evaluation of the in vitro biocompatibility of a new fast-setting ready-to-use root filling and repair material[J]. Int Endod J, 2017, 50(6): 540-548.
[38] 乔迪, 董艳梅, 高学军. 体外评价新型根尖倒充填材料iRoot的生物学性能[J]. 北京大学学报(医学版), 2016, 48(2): 324-329.
[39] Mozayeni MA, Milani AS, Marvasti LA, et al.Cytotoxicity of Calcium enriched mixture cement compared with mineral trioxide aggregate and intermediate restorative material[J]. Aust Endod J, 2012, 38(2): 70-75.
[40] Razmi H, Aminsobhani M, Bolhari B, et al.Calcium enriched mixture and mineral trioxide aggregate activities against enterococcus faecalis in presence of dentin[J]. Iran Endod J, 2013, 8(4): 191-196.
[41] Rahimi S, Mokhtari H, Shahi S, et al.Osseous reaction to implantation of two endodontic cements: Mineral trioxide aggregate (MTA) and Calcium enriched mixture (CEM)[J]. Med Oral Patol Oral Cir Bucal, 2012, 17(5): e907-e911.
[42] Asgary S, Nosrat A, Homayounfar N.Periapical healing after direct pulp capping with calcium-enriched mixture cement: a case report[J]. Oper Dent, 2012, 37(6): 571-575.
[43] Asgary S, Eghbal MJ, Ghoddusi J, et al.One-year results of vital pulp therapy in permanent molars with irreversible pulpitis: an ongoing multicenter, randomized, non-inferiority clinical trial[J]. Clin Oral Investig, 2013, 17(2): 431-439.
[44] Nosrat A, Seifi A, Asgary S.Pulpotomy in caries-exposed immature permanent molars using calcium-enriched mixture cement or mineral trioxide aggregate: a randomized clinical trial[J]. Int J Paediatr Dent, 2013, 23(1): 56-63.
[45] Poggio C, Beltrami R, Colombo M, et al.In vitro antibacterial activity of different pulp capping materials[J]. Clin Exp Dent, 2015, 7(5): e584-e588.
[46] Lee BN, Lee BG, Chang HS, et al.Effects of a novel light-curable material on odontoblastic differentiation of human dental pulp cells[J]. Int Endod J, 2017, 50(5): 464-471.
[47] Gandolfi MG, Siboni F, Prati C.Chemical-physical properties of TheraCal, a novel light-curable MTA-like material for pulp capping[J]. Int Endod J, 2012, 45(6): 571-579.
[48] Camilleri J.Hydration characteristics of Biodentine and Theracal used as pulp capping materials[J]. Dent Mater, 2014, 30(7): 709-715.
[49] Alzraikat H, Taha NA, Qasrawi D, et al.Shear bond strength of a novel light cured calcium silicate based-cement to resin composite using different adhesive systems[J]. Dent Mater J, 2016, 35(6): 881-887.
[1] 冯靓婧(综述), 于皓, 程辉(审校). 不同染色方法对氧化锆陶瓷性能的影响[J]. 口腔疾病防治, 2018, 26(5): 334-337.
[2] 文静, 洪席超, 郜文秀, 黄锋. MTA 用于年轻恒前牙直接盖髓术的临床效果观察[J]. 口腔疾病防治, 2017, 25(5): 320-322.
[3] 丁祥龙 综述; 周磊 审校. TiO2光催化效应对种植体生物活性的影响[J]. 口腔疾病防治, 2016, 24(1): 49-52.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
[1] 李文妙 综述, 朴正根 审校. 氢氧化钙封药载体的研究进展[J]. 口腔疾病防治, 2017, 25(3): 192 -195 .
[2] 李梦琪 综述, 蓝海 审校. 防龋材料的研究进展[J]. 口腔疾病防治, 2017, 25(10): 668 -671 .
[3] 龙明生, 瞿小维, 董红. 口腔内窥镜联合超声技术寻找隐匿性根管的效果观察[J]. 口腔疾病防治, 2017, 25(11): 733 -736 .
[4] 叶青松, 王晓燕. 牙源性干细胞储存和临床应用的研究进展[J]. 口腔疾病防治, 2018, 26(1): 15 -25 .
[5] 刘军平, 易晨, 王建广. 经口内横断冠状突取出颞下窝与翼腭窝异物的临床回顾性分析[J]. 口腔疾病防治, 2018, 26(4): 231 -235 .
[6] 王晓瑾, 游昕超, 陈凯, 黄坤宋, 潘宣. 木犀草素对人舌鳞癌细胞侵袭和迁移的影响[J]. 口腔疾病防治, 2018, 26(7): 434 -439 .